It is applicable to the addition of target alloy elements in the smelting process of non-ferrous metals, and effectively adjust the component content of alloy products. The product has uniform composition, stable quality and high element yield; Rich variety.
characteristic:
Nickel, flux and aluminum are mixed, and the nickel content is 75%-95%.
Applicable to the configuration of aluminum nickel alloy.
When used correctly, the recovery rate is stable above 95%.
The storage period is more than ten months (stored in a dry place).
Usage:
Adjust the temperature of molten aluminum not lower than 700 ℃, and the appropriate temperature not lower than 730 ℃.
According to the composition standard of the alloy, calculate the required dosage, and use the saw blade to divide the additive block.
Dry the aluminum slag, throw the additive blocks into the molten aluminum as far as possible, and stir them slightly.
Stir for about 3-5 minutes until manganese is evenly dispersed.
Key points:
Temperature, dispersion and mixing.
Specifications:
Each piece weighs 500g, and the mini piece weighs 200g.
packing:
Packed in 20kg/ carton, 2kg/ inner plastic bag, or 10kg kraft paper bag
be careful:
It should not be thrown on the inner wall of the furnace, nor should it be placed in one place in the molten aluminum.
The unpacked additive blocks shall be used up within five days as far as possible, and the ones after unpacking shall be
It can be used up in a month. Always store in a dry place.